ALUMINIUM TRIHYDRATE (ATH) is a very finely grounded product having a uniform and controlled particle size distribution. Aluminium Trihydrate is the most effective low-cost Flame Retardant filler and is mainly used as a FLAME RETARDANT & SMOKE SUPPRESSANT in various Plastics & Rubber Applications. TYPICAL CHEMICAL ANALYSIS:- PROPERTIES ANALYSIS A1 (OH3) 99.50% Max A12O3 64.50% Min FE2O3 0.01% Max SiO2 0.01% Max Na2O (Total) 0.25% Max TYPICAL PHYSICAL PROPERTIES:- PROPERTIES ANALYSIS Specific Gravity 2.40+=0.02 Loss On Ignition 34.50% Max (1100 Deg C) Moisture Content 0.50% Max (105 Deg C) Coatings Available Silane & Stearic Average Particle Size 2.00-80.00 Mic (d50) (As Per Grade)

FAM - 501 Flame Retardant filler FAM-501 is One Pack Flame Retardant & Smoke Suppressant developed for Plasticized PVC applications. It is an Aluminum & Magnesium inorganic complex synergist treated with dispersing aids which results in the superior dispersion, processability and compatibility with the polymer hence imparting superior flame retardant & Smoke Suppressant properties as compared to other traditional synergists, especially in PVC. The synergy of FAM-501 has also been reported along with a high dosage of ATH in FRLS PVC Formulations. TYPICAL SPECIFICATIONS:- PROPERTIES ANALYSIS Appearance White Powder Moisture 0.40% Max (105 deg C) Bulk Density 0.40 - 0.45 gm/cc (Untapped) Specific Gravity 2.38 += 0.02 Sieve Residue Nil (at 325 Mesh) Average Particle 1.50-2.50 Microns Size d50 (By Laser Diffraction)

MAGNESIUM HYDROXIDE is a very finely grounded product having an extremely uniform and narrow particle size distribution. It is considered as a non halogenated, environment friendly and non toxic mineral based flame retardant & smoke suppressant. It is used in various plastics & rubber applications. The initial Decomposition Temperature of Magnesium Hydroxide is 320° C making it suitable for applications where the usage of Aluminium Trihydrate (ATH) has a limitation due to a higher polymer processing temperature of more than l 80°C. Due to its higher Decomposition Temperature than ATH, It is being used as an effective smoke suppressant in conjunction with ATH. TYPICAL CHEMICAL ANALYSIS:- PROPERTIES ANALYSIS Mg (OH2) 93.00% Min MgO 60.0-62.0% CaO 2.00-2.50% SiO2 1.00-1.50% Fe2O3 0.10-0.20% TYPICAL PHYSICAL ANALYSIS:- PROPERTIES ANALYSIS Specific Gravity 2.36+=0.02 Loss On Ignition 31.00%Max Max (1100 Deg C) Moisture Content 0.50% Max (105 Deg C) Coatings Available Silane & Stearic Average Particle Size (d50 By Laser Diffraction

CALCIUM BORATE is characterized as an environmentally friendly mineral based Flame Retardant Synergist developed as an alternative to Synthetic Zinc Borate in order to solve the thermal stability problem accompanied by Zinc Borate in plasticized PVC Applications, along with imparting superior Flame Retardant properties comparatively to Zinc Borate. The Flame Retardant action of Calcium Borate is mainly based upon its high Char Forming and Glazing/ Fluxing ability in combination with endothermic decomposition (Heat-Shrink Effect) and along with its inert water content (Loss on Ignition) which is quite higher as compared to traditional Zinc Borate which gives it an edge over it. TYPICAL CHEMICAL ANALYSIS PROPERTIES ANALYSIS CaO Content 32+=1.50% (By Weight) B2O3 Content 44+=1.50% (By Weight) 0.30% Max MgO TYPICAL PHYSICAL PROPERTIES PROPERTIES ANALYSIS Appearance White Powder Sieve Residue 0.10% Max (at 325 Mesh) Loss On Ignition 23.6+=1.50% (450 deg C) Moisture Content 0.40% Max Average Particle Size 2.5-3.5 Mic (By Laser Diffraction)

FLAMEX is a proprietary one pack flame retardant synergist treated with processing & dispersion aids which imparts superior flame retardant properties as compared to traditional flame retardant synergists. It can meet the required UL standard and achieve the V0, V1, V2 flammability rating. We have various grades of FLAMEX which are HALOGEN FREE or halogen containing also as per requiremts in which polymer it has to be used and what properties of final product is required. Various applications of FLAMEX include polyolefins, engineering plastics, HDPE, LDPE, PPCP, PPHP, XLPE, ABS, PBT, Nylon, Nylon-66, EVA, Rubber, UPR etc. FLAMEX manufactured by our company is widely used in Automotive and Transportation, Building and Construction, Electrics and Electronics, Upholstery etc. PP,PA, PE,PC ,PC/ABS, PVC , Rubber ,PBT, PET, XPS, EPS, PU ,PVC, coating, textile include polyolefins, engineering plastics, HDPE, LDPE, PPCP, PPHP, XLPE, ABS, PBT, Nylon, Tapes, PVC, Leader Cloths, Nylon-66, EVA, PU Form, EPF Form, Textiles, Rubber, UPR etc. Replacement of Antimony Trioxide is a proprietary flame-retardant synergist developed for plasticized and rigid PVC applications as a cost effective complete replacement of Antimony Trioxide. It is an Antimony based inorganic complex synergist treated with processing and dispersion aids-which imparts superior flame retardant properties as a replacement of traditional flame-retardant synergists. Few applications include PVC Wire & Cable Compound, PVC Conveyor Belts, PVC Leather Cloth, PVC Calendaring sheets, PVC Tubing. PVC Cladding, PVC Hoses etc .